光学系统用铝合金材料的硬质氧化工艺

放大字体  缩小字体发布日期:2012-04-19  浏览次数:690

摘要:采用先硬质氧化再染黑色的方法对光学系统用铝合金材料进行了处理。检测了氧化膜层的厚度、显微硬度和反射率,分析了溶液成分、电流密度、温度和氧化时间对氧化膜反射率的影响。结果表明,采用含260~3009几硫酸、l0~15 9/L草酸和l0~20 9/L多元醇的溶液在温度5~7 ℃、电流密度2~3 A/dm2的条件下氧化50 min,可获得厚度l5 um、显微硬度450 HV、反射率低于8.4%的硬质氧化膜层,该氧化膜适用于高精度军用光学变焦系统。

 

关键词:光学变焦系统;铝合金;硬质氧化;显微硬度;反射率

 

中图分类号;TGl74.41;TQl53.6   文献标志码:A

 

文章编号:1004—227X(2009)03—0024—03

 

Hard anodizing process on aluminum alloy materials for optical system//JIANG Wei*,SHEN De-xin,WANG Li-bo

 

AbstractA method of hard anodizing followed by black dyeing was used to treat aluminum alloys for optical system.The thickness,microhardness and reflectance of oxide film were measured.and the effects of solution composition.current density,temperature and oxidation time on reflectance of oxide film were analyzed.The results showed tllat a hard oxide film with thickness of l 5μm.micro— hardness of 450 HV and reflectance below 8.4%can be obtained in a solution containing 260.300 g/L sulfuric acid.1 0-1 5∥L oxalic acid and l 0-20 g/L polyol at temperature5—7℃and current density 2.3 A/dm2.The oxide film iS suitable for military optical zoom system with high precision.

 

Keywordsoptical zoom system;aluminum alloy;hard anodizing;microhardness;reflectance

 

First-author’s addressChangchun UP Optotech C0.,Ltd.,Changchun l30031,China

 

1  前言

 

   随着国防工业的不断发展,光电仪器的应用日益广泛。为了监视、测量和跟踪目标的弹道和轨道,常需采用可连续变焦的光学系统。而变焦机构是连续变焦系统的核心部件,对系统的跟踪精度[1]、成像质量等有显著影响。变焦机构由凸轮、滑架和导轨架组成,为保证光学系统的可靠运行、减少光路杂散光,上述零件应具有一定的硬度和较低的镜面反射率。本文对变焦机构零件所用的7A04铝合金材料进行硬质氧化处理后染黑,测定了硬质氧化处理后所得氧化膜的厚度、显微硬度和镜面反射率,以期能够满足军用光学系统对铝合金材料性能和可靠性的要求。