分光光度法测定锡钻合金镀液中的钴:前言

放大字体  缩小字体发布日期:2012-04-16  浏览次数:670

摘要:pH=10的柠檬酸铵一氨水溶液中,钴与苦氨酸偶氮变色酸反应形成绿色配合物,其最大吸收波长为650 nlTl,表观摩尔吸光系数为2.62×104 L/(mol·cm)。在25 mL溶液中,钴含量在0~50Ix9范围内遵循比尔定律。样品分析表明,该法的相对标准偏差小于2%。

关键词:锡钴合金;镀液;钴;测定;苦氨酸偶氮变色酸;分光光度法

中图分类号:T0657.32    文献标志码:A

文章编号:1004—227X(2009)05—0035—02

Speetrophotometric determination  of cobalt in tin-cobalt ahoy plating solution with picramazochrom//ZHONG Guo-xiu+,YANG Hao-yi,YAN Ga0—hua

AbstractCobalt reacts with picramazochrom to form a green complex with a apparent molar absorption coefficient.of 2.62×104L/(mol·cm)at the wavelength of 650 nlTI in a solution consisting of ammonium citrate and ammonia at pH 10.Beer’S law is obeyed in the range of0—50 μg cobalt in a 25 mL bath.Sample analysis showed that the relative standard deviation was less than 2%.

Keywordstin——cobalt alloy;plating bath;cobalt;determination;picramazochrom;spectrophotometry

First-author’S addressHubei Reserch&Design Institute ofMechanical Electronic Engineering,Wuhan 430070,China

 

前言

 

    锡钻合金镀层具有优良的耐蚀性和抗变色性,较高的硬度和较低的内应力,镀层基本无空隙,覆盖能力优良,因此在滚镀方面可代替操作要求苛刻的滚镀铬,并已应用于无耐磨要求的代铬镀层[1-2]。镀层中钻含量在20%左右时,镀层外观接近铬;钴含量低于20%时,镀层呈光亮的白色;钴含量高于20%时,外观为枪黑色或黑色。因此,生产中监测镀液中钴含量的高低具有重要意义。

 

    锡钴合金镀液中钻的测定方法主要有分光光度法[3-4]、滴定法[5]等。苦氨酸偶氮变色酸已用于测定钢铁[6]及铝合金[7]中的钴含量,本文尝试将其应用于锡钴镀液中钴的测定。同时,以柠檬酸铵一氨水溶液作为显色介质并掩蔽其他共存元素(尤其是铁)的干扰,收到了较好的效果。该法简单快速,结果准确可靠。

 

分光光度法测定锡钻合金镀液中的钴:实验

分光光度法测定锡钻合金镀液中的钴:结果与讨论

分光光度法测定锡钻合金镀液中的钴:结论